MariaT wrote:
The bad news? I cannot get the plasterite out of the vase which has cracked despite being made of quite thick glass. Any suggestions?
Maria, I’m new to orgonite myself, but thought I’d share (if it hasn’t already been mentioned, and you may already know 
) that as plaster hardens it gets very hot, so I’m not surprised the thick glass has broken. I used to make plaster molds for ceramics, so came across that then. Maybe if any thick glass molds were heated, they wouldn’t crack so easily? In making molds (for ceramics), I’d put the plaster on the outside of the item, not inside as in making plasterite orgonite, so I didn’t have the expansion issue that seems to be happening.
this information may be extremely useless … hope not, though …
I like the energy of the one that is out of the mold … it feels clear and clearing …
& thanks, Josh, for your reply to my question .. 